TS11490F 8 Hours Fast Curing Wear Compound Filled with Ceramic Balls and Silicon Carbide
Product Features:
TS11490F is fast curing anti-abrasive epoxy coating, it contains big ceramic pearls and silicon carbide. Two components, A-part is epoxy resin and B-part is curing agent. It's grey color after mixing. It has good bonding strength with base materials. TS11490F has excellent wear resistance and corrosion resistance. It has medium viscosity, easy to operate with tools, fast curing at room temperature.
Product Application:
TS11490F wear compound is widely used in large area repair and protecting high load machinery and equipment which are eroded by particles over 3mm frequently. Application areas includes pipeline elbows, chutes,slurry pump, cyclones, fly ash separators, screw conveyors etc.
Technical Data:
| Product name |
Color |
Appearance |
Volume
(cm3) |
Operating time
(25ºC) |
Curing time
(25ºC) |
| TS11490F wearing compound |
Grey |
Paste |
4100 |
20min |
8h |
Density
(g/cm3) |
Compressive strength
(kg/cm2)
GB1041-2008 |
Tensile strength
(kg/cm2)
GB6329-1999 |
Shear strength
(kg/cm2)
GB7124-2009 |
Flexural Strength
(kg/cm2)
GB1042-2008 |
Hardness
(Shore D)
ASTM-D-2556 |
Working temperature
(ºC) |
| 2.42 |
981 |
367 |
146 |
508 |
89 |
-60~150 |
How to use:
1, surface treatment: Roughing Treatment: Grinding or sandblasting the parts to be treated by angle grinder; Then clean the parts surface, the surface should be clean and dry without oil or dust.
2,mixing: The TS11490F wear compound mix ratio is A:B=2:1 by weight. Mix two component well and use up the coating within 20 minutes. Don't mix the coating over 1.5kg one time in summer, because mix too much epoxy coating will make curing time faster, thus users will not use up the coating in time. In winter, users can mix over 1.5kg coating depend on the temperature. If temperature is low, user can heat the A-part resin to make viscosity lower so to speed up the curing time.
3, coating: The suitable thickness of TS11490F is 4-8mm. Mixed coating should be coated layer by layer on the parts to be repaired. The first layer should be compacted so that it can be fully infiltrated with the base material.After finish the coating, the part surface shall be smoothed out.
4, curing: Curing time is 8 hours at 25ºC. If temperature is low, users can use heat treatment to speed up the curing time. In winter, we suggest to use iodine tungsten lamp to heat the coating. Lamp and coating spacing is 40cm.
Packing: 5kg/set, 10kg/set and 20kg/set
Transport and storage: Keep the product in dry, cool and covered facility, shelf life is 2 years. Avoid inversion and collision in transportation. This product is non dangerous goods.