10kg/Set Anti-Abrasive Compound Wear Resistant Compound

• Customization: Available
• CAS No.: 7085-85-0
• Formula: Mixture
• Model NO.: TS11490F
• EINECS: 230-391-5
• Bonding Function: Structural Adhesive
• Morphology: Paste
• Application: Construction, Woodworking, Footwear & Leather, Fiber & Garment, Packing
• Material: Epoxy
• Classification: Room Curing
• Main Agent Composition: Epoxy Resin
• Characteristic: Waterproof
• Promoter Composition: Curing Agent
• Composition: Organic Material
• Color: Grey
• Free Sample: Yes, Buyer Need Pay Freight
• OEM Service: Yes
• Certificate: MSDS, TDS
• Shelf Life: 1 Year
• Transport Package: 10kg/Drum
• Specification: 10kg/set, 20kg/set
• Trademark: Customized
• Origin: China
• HS Code: 3214109000
• Production Capacity: 30000tons/Month

Product Description

TS11490F 8 hours curing ceramic bead filled wear compound



Product Description:

High-density, alumina ceramic bead-filled, toughened epoxy system for repairing and protecting equipment from wear and abrasion caused by handling and processing particulate matter as solid or in slurry form.

Product Features:
 

1.ceramic-filled for outstanding resistance to abrasion

2.Renews worn surfaces fast-reduces downtime

3.Extends wear life- resists sliding abrasive wear and eliminates costly wear part inventory

4.Non sag- provides abrasion resistance on over-head and vertical surfaces.

Product Application:

1.Cyclone and separator bodies

2.Dust collectors and exhausters

3.Pump liners and impellers

4.Fan blades and housings

5.Chutes and hoppers

6.Elbows and transition points

Technical Data:
 

Color:	Grey
Specific gravity:	2.43g/cm³
Mix ratio by weight:	8:1
Mix ratio by volume:	4:1
Working time(min):	65min
Compressive strength(GB/T1041):	112.0MPa
Tensile strength(GB/T6329):	32.0MPa
Shear strength(GB/T7124):	14.0MPa
Flexural strength(GB/T9341):	45.0MPa
Fully cured time:	24h
Temperature range:	-60~160ºC

How to Use:

1. Surface treatment:
roughening the parts to be treated, sanding or sandblasting with an angle grinder, etc.; cleaning the roughened surface; the treated surface should be a rough and dry fresh substrate surface, and should be No oil and dust.
2. Preparation:
Mix the components A and B of the small particle wear-resistant protective agent according to the mass ratio A:B=4:1, and use them within 30 minutes.
3. Coating:
apply the uniformly mixed small particles of wear-resistant protective agent layer by layer to the area to be repaired, preferably at a thickness of 3-10 mm. The adhesive layer should be compacted to fully infiltrate the substrate; after the coating is applied to the required size, the surface layer is smoothed.
4. Curing:
Curing at 25ºC for 16 hours can be put into use. When the temperature is lower than 10 degrees, it can be cured by baking with an iodine tungsten lamp or electric heating plate for 2 hours.


Packing:

500g/set,  10kg/set 


Transport and storage:

Keep the epoxy coating in dry, cool and covered facility, shelf life is 1 year. Avoid inversion and collision in transportation. This product is not dangerous goods.