Rubber to Rubber Cold Bonding Cement Adhesive Tiptop Sc2000 Replacement

• CAS No.: 7085-85-0
• Formula: Chloroprene Rubber
• EINECS: 230-391-5
• Bonding Function: Structural Adhesive
• Morphology: Paste
• Application: Construction, Woodworking, Footwear & Leather, Fiber & Garment, Packing
• Model NO.: TS2000
• Material: Chloroprene Rubber
• Classification: Room Curing
• Main Agent Composition: Chloroprene Rubber
• Characteristic: Waterproof
• Promoter Composition: Curing Agent
• Composition: Organic Material
• Color: Black
• OEM Service: Yes
• Sample to Test: Yes
• Shelf Life: 18 Months
• Certificate: MSDS, Testing Report
• Transport Package: 10 Sets/Carton
• Specification: 1kg/set
• Trademark: Customized
• Origin: China
• HS Code: 3214109000
• Production Capacity: 500000PCS/Month

Product Description

Conveyor belt cold vulcanizing cement TS2000, 1kg/set(with adhesive and hardener). Can replace Tiptop SC2000




Product Application:

Conveyor belt cold vulcanizing cement TS2000, two-component adhesive,it's the ideal conveyor belt damage repair cement when bonding rubber to rubber,rubber to fabric, rubber to metal and fabric to fabric bonding, or used in corrosion and wear protection applications for conveyor belt applications.


 

Product Features:

1 Non-flammable.

2 Fast speed of solidifying(curing time can be 2 hours), high intension, anticorrosion, resistance to aging in normal temperature.

3.Easy operation and low cost. 

How to use:
1, Surface treatment: Deburring the parts to be bonded. Clean and dry the parts.
2, Mix: Pour the B-part into A-part directly and stir them quickly. Then, pour the mixed adhesive to the parts.
3, Curing: Curing time is 2 hours at room temperature. After 24 hours, it can get to highest bonding strength.
 
Technical data sheet:

Part No.	Color	Appearance	Density(g/cm³)	Peel strength(N/cm) GB/T2791-1995	Mix ratio	Operating time(min)	Curing time	Heat resistant(°C)
TS2000	Black	Liquid	0.9-1.3	120	A:B=100:5	20-40	2 hours	100

 
 
Packing:

1kg/set, 10sets/carton;