Metal Filled Epoxy Iron Putty 111 for Iron Repair

• Customization: Available
• CAS No.: 7085-85-0
• Formula: Mixture
• Model NO.: 111
• Bonding Function: Structural Adhesive
• Morphology: Paste
• Application: Construction, Woodworking, Footwear & Leather, Fiber & Garment, Packing
• Material: Epoxy
• Classification: Room Curing
• Main Agent Composition: Epoxy Resin
• Characteristic: Waterproof
• Promoter Composition: Curing Agent
• Composition: Organic Material
• Color: Cast Iron
• Package Available: 500g, 5kg, 10kg
• Shelf Life: 1 Year
• Sample to Test: Yes
• OEM Service: Yes
• Transport Package: Paper Carton
• Specification: 500g/set
• Trademark: Customized
• Origin: China
• HS Code: 3214109000
• Production Capacity: 500000sets/Month

Product Description

111  Epoxy Putty for repairing casting iron, it can 100% replace Fuller Tonsan 111.


Product Pictures:




Product features:

 

Double components, high strength, metal-filled epoxy putty. Suitable for repairing and restoring of blowholes, shrinkage, flow marks and cracks in iron casting parts.

Product Applications:





Physical Properties: 

Color:	Cast iron
Specific gravity:	1.62g/cm³
Mix ratio by weight:	7:1
Mix ratio by volume:	4:1
Working time(min):	60min
Compressive strength(GB/T1041):	110.0MPa
Tensile strength(GB/T6329):	42.0MPa
Shear strength(GB/T7124):	20.0MPa
Flexural strength(GB/T9341):	70.0MPa
Hardness(GB/T2411):	82Shore D
Cured time for machining:	24h
Temperature range:	-60~160ºC

How to use:
 
1.Surface Cleaning:
 Remove the oil and grease from the surface, also should be abrasived and polished.
 
2. Mixing
 Two-part, please mix and forge the two parts by equal ratio. It will become gel-formulation at the low temperature, it can change into soft gel heating by the heating producer.
 Notice: Do not heat with the open-fire
After 24 h room cure, it can put into use.
 
3.Coating
 First, coating the surfaces with some glue, and then push and repeat coating the surface until it exhaust the air and fully fill the gap. 
 
4.Curing
 When the room temperature is lower than 10°C, and after 1-2 h room cure, use heat producer heating for 3-4 hour bewteen 80°C, the heating producer between the parts should keep a distance of 300-400mm. and the small-area fittings can be put into the oven for heating below 80°C.
 (Heat Producer: infra-red lamp, electric stove, and other heating sources, not use the open-fire)
 
 5.Post-Processing
 After cured some time, it can be processed by ordinary ways, and wait for 18 hour, it can use the machine for processing.



Attention:


1,When the temperature is below 15 ºC, some heating measures should be adopted; or the relevant curing time should be extended

2,When mix volume is more than 200g, the working time will be shorter

3,Above data is typical



Package:
500g/set, 16sets/carton
10kg/drum or customized