Conveyor Belt Cold Jointing Cement Cold Vulcanizing Cement Cold Adhesive Ts2000

• CAS No.: 7085-85-0
• Formula: Chloroprene Rubber
• EINECS: 230-391-5
• Bonding Function: Structural Adhesive
• Morphology: Paste
• Application: Construction, Woodworking, Footwear & Leather, Fiber & Garment, Packing
• Model NO.: TS2000
• Material: Chloroprene Rubber
• Classification: Room Curing
• Main Agent Composition: Chloroprene Rubber
• Characteristic: Waterproof
• Promoter Composition: Curing Agent
• Composition: Organic Material
• Color: Grey
• Shelf Life: 18 Months
• Sample to Test: Yes
• OEM Service: Yes
• Certificate: MSDS
• Transport Package: 10 Sets/Carton
• Specification: 1kg/set
• Trademark: Customized
• Origin: China
• HS Code: 3214109000
• Production Capacity: 500000PCS/Month

Product Description

TS2000 Type Conveyor Belt Bonding Adhesive, Can Repalce Tiptop SC2000 Cold Bond Cement



TS2000 is cold vulcanized splicing cement. Double components, high strength, good flexibility adhesive. Applied for self-adhesion or bonding between conveyor, rubber, fabric, leather. Peeling strength at bonding area is higher than combination strength between rubber and fabric. 1000g/set, 10sets/carton.
 

Product Features:

1 Non-flammable.

2 Fast speed of solidifying, high intension, anticorrosion, resistance to aging in normal temperature.

3.Easy operation and low cost. 

How to use:
Surface treatment: roughening the belt by steel wire wheel, then use cleaner to clean the belt and dry it.
Mixing: Pour the B-part hardener to A-part adhesive, and mix them well.
Gluing: Use brush to apply adhesive on the belt in three times
Dry: Every time after gluing, to speed up the curing time to 30 min, user can use Iodine tungsten lamp or infrared lamp to bake the cement until it's tack-free(bake temperature shall be 60ºC to 80ºC), then apply glue again.
Bonding: After the third time to apply the adhesive and tack-free, users can use hand hammer to beat the belt and adhesive until they are dense.

 
Technical data sheet:

Part No.	Color	Appearance	Density(g/cm³)	Peel strength(N/cm) GB/T2791-1995	Mix ratio	Operating time(min)	Curing time	Heat resistant(°C)
TS2000	Black	Liquid	0.9-1.3	110	A:B=100:4	20-40	2 hours	100

 
 
Packing:

1kg/set, 10sets/carton;
700g/set, 10set/carton